Bendable Metal Strips Ribbon In Magnetic

We are Manufacturer and Exporter of Bendable Metal Strips Ribbon in Magnetic in Zhengzhou, Henan, China.


Product Introduction
1 Introduction

Iron Based Nano crystalline Ribbon is composed of Fe, Si, B, Nb, and Cu etc.
Iron based amorphous alloy including Cu and Nb element can be formed into crystallite with size in 10-20nm above crystallization temperature through particular annealing treatment. The crystallite material is defined as Nano crystalline alloy.

2 Application

EMC common mode and differential mode filter inductor cores;
switching-mode power supply transformer cores;
current mutual sensor cores (zero sequence, leakage protection);
Magnetic amplifier, spike killer core, saturable inductor core;

3 Feature

High saturation flux density, high permeability, low coercivity, Low loss, good stability, high strength and corrosion resistance, can replace silicon steel, permalloy and ferrite as ideal material for transformer, mutual inductor, its components, has the highest PQ ratio.
Specification
Saturation Flux Density Bs /T1.25 Saturation magnetostriction I s27*10^-6
Curie Temperature Tc(a )560 Density d (g/cm^3)7.2
Crystallization A Tx(a )510 Resistivity I (ICmA /m)130
Hardness HV (kg/mm^2)880 Thickness um29-35


Thickness um0.020-0.025 Filling Factor I a Y0.80
Magnetic Displacement Bi Ta Y1.12 Coercivity Hc(A/m)a 2.0
Iron Loss P0.5T/20kA (W/kg)A a 25 Iron Loss P0.3T/100kA /(W/kg)A a 100
Permeability u(1khz)a Y70000 Permeability u(10khz)a Y60000
Permeability u(100khz)a Y10000 Curie Temperature Tca 570
Continuous Operation Temp a -50-120 Saturation Magnetostriction I s<2*10A -6


Performance Advantages & Feature
High saturation flux density-- to reduce winding turns, minimize product size

High resistivity, low coercivity--to improve production performance

Low loss(1/3 to 1/5 of silicon sheet)--to cool temperature, improve efficiency
Low excitation--decrease no-load current, and noise

Adjustable permeability--adopt different heat treatment process according to different requirement
High temperature stability--long-term operation under 130A C